Home Subscription Services
 
   

 
The Journal of Adhesive Dentistry
JAD Home Page
About the Editor
Editorial Board
Submit
Author Guidelines
Submission Form
Reprints / Articles
Permissions
Advertising
Advertising
MEDLINE Search
 
 
 
 
 
FacebookTwitter
Quintessence Publishing: Journals: JAD

 

The Journal of Adhesive Dentistry

Edited by Prof. Dr. Roland Frankenberger, Prof. Bart Van Meerbeek

ISSN (print) 1461-5185 • ISSN (online) 1757-9988

Publication:

September/October 2021
Volume 23 , Issue 5



Pages: 469–475
Back
Share Abstract:

Composite Cement Components Stabilize the Bond between a Lithium-Disilicate Glass-Ceramic and the Titanium Abutment

Han-Gyul Sung / Kyung-Ho Ko / Chan-Jin Park / Lee-Ra Cho / Yoon-Hyuk Huh

Purpose: To evaluate the effect of composite cement components and thermocycling on the bond strength of monolithic lithium-disilicate (LS2) glass-ceramic implant-supported restorations bonded to titanium (Ti) abutments. Materials and Methods: Eighty LS2 blocks were treated with five types of composite cement and primer, then divided accordingly into groups: M (Multilink hybrid abutment), G (G-CEM LinkAce), GP (G-CEM LinkAce with G-Multi PRIMER), P (Panavia F2.0), and U (RelyX U200). Half of the 16 specimens from each group were subjected to thermocycling (groups T-M, T-G, T-GP, T-P, and T-U). The tensile bond strength (TBS) of all specimens was measured using a pull-off test. The cross section of the LS2 block from which the Ti abutment was removed was examined for mode of failure. Two-way ANOVA and Tukey’s HSD test (significance level = 0.05) were used to determine the effect of composite cement composition and thermocycling on TBS. Results: There was no difference in TBS between the five groups before thermocycling (p = 0.16). However, groups M (p < 0.001) and G (p = 0.014) showed significantly lower TBS than the corresponding thermocycled groups. Groups T-GP, T-P, and T-U did not show significant changes in TBS after thermocycling (p > 0.05). All failures occurred at the interface between the composite cement and Ti abutment and not between the cement and the LS2 block. Conclusion: Thermocycling can reduce the bond strength between the composite cements and Ti abutment. The composite cements containing 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) or methacrylate phosphate ester monomers stabilize bonding.

Full Text PDF File | Order Article

 

 
  © 2021 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog