Home Subscription Services
 
   

 
The Journal of Adhesive Dentistry
JAD Home Page
About the Editor
Editorial Board
Submit
Author Guidelines
Submission Form
Reprints / Articles
Permissions
Advertising
Advertising
MEDLINE Search
 
 
 
 
 
FacebookTwitter
Quintessence Publishing: Journals: JAD

 

The Journal of Adhesive Dentistry

Edited by Prof. Dr. Roland Frankenberger, Prof. Bart Van Meerbeek

ISSN (print) 1461-5185 • ISSN (online) 1757-9988

Publication:

September/October 2021
Volume 23 , Issue 5



Pages: 409–420
Back
Share Abstract:

Microtensile Bond Strength, Bonding Interface Morphology, Adhesive Resin Infiltration, and Marginal Adaptation of Bulk-fill Composites Placed Using Different Adhesives

Maicon Sebold / Rodrigo Barros Esteves Lins / Beatriz Ometto Sahadi / Marina Rodrigues Santi / Luís Roberto Marcondes Martins / Marcelo Giannini

Purpose: This study evaluated dentin bond strength, failure mode, interface morphology, adhesive infiltration into dentin, and marginal adaptation of bulk-fill composites used with different adhesives. Materials and Methods: Third molars received occlusal class I cavities (4 mm x 4 mm x 4 mm) that were bulk-filled with Admira Fusion x-tra (Voco) or SonicFill 2 (Kerr) using four adhesives (Scotchbond Multipurpose, 3M Oral Care; Clearfil SE Bond, Kuraray Noritake; OptiBond All-In-One, Kerr; Futurabond U, Voco). Scotchbond was used with acid-etching, while the remaining adhesives were applied in self-etch mode. Sixty-four teeth were selected for the microtensile bond strength test (n = 8). Failure modes were analyzed with scanning electron microscopy (SEM). Interface morphology and adhesive infiltration (n = 3) were investigated using confocal laser scanning microscopy (CLSM). Marginal adaptation (n = 3) was also evaluated using SEM. Bond strength, failure mode, and adhesive infiltration data were analyzed for distribution and homocedasticity, followed by appropriate statistical analyses (α = 0.05). Results: Regarding bond strength, no differences were found among adhesives for SonicFill; Clearfil showed a significantly lower mean value than did Scotchbond (p ≤ 0.05) for Admira; the two composites did not differ. Adhesive and mixed failures were observed for all groups. Scotchbond led to thicker hybrid layers with deeper adhesive infiltration as opposed to Futurabond. The groups Admira+Futurabond, SonicFill+Clearfil, and SonicFill+Futurabond presented the highest marginal discontinuity. Conclusion: The tested bulk-fill composites did not affect dentin bonding. Scotchbond and Clearfil seem to be reliable for bonding SonicFill 2 to dentin. The performance of Futurabond was questionable, given its poor-quality interface and higher percentages of marginal gaps.

Full Text PDF File | Order Article

 

 
  © 2021 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog