Home Subscription Services
 
   

 
The Journal of Adhesive Dentistry
JAD Home Page
About the Editor
Editorial Board
Submit
Author Guidelines
Submission Form
Reprints / Articles
Permissions
Advertising
Advertising
MEDLINE Search
 
 
 
 
 
FacebookTwitter
Quintessence Publishing: Journals: JAD

 

The Journal of Adhesive Dentistry

Edited by Prof. Dr. Roland Frankenberger, Prof. Bart Van Meerbeek

ISSN (print) 1461-5185 • ISSN (online) 1757-9988

Publication:

September/October 2015
Volume 17 , Issue 5



Pages: 413–419
PMID: 26525005
DOI: 10.3290/j.jad.a35011
Back
Share Abstract:

Aging Effect of Atmospheric Air on Zirconia Surfaces Treated by Nonthermal Plasma

Daniela Micheline dos Santos / Aljomar José Vechiato-Filho / Emily Vivianne Freitas da Silva / Marcelo Coelho Goiato / Paulo Francisco Cesar / Elidiane Cipriano Rangel / Nilson Cristino da Cruz

Purpose: The purpose of this study was twofold: 1) to characterize the zirconia (Y-TZP) surfaces through scanning electronic microscopy associated with energy-dispersive spectroscopy and atomic force microscopy after the deposition of a thin organosilicon film by nonthermal plasma (NTP) treatment, and 2) to determine the zirconia surface hydrophilicity, before and after aging, through surface energy analysis.

Materials and Methods: Surfaces of 16 zirconia disks (10 x 3 mm) were treated for 30 min each with hexamethyldisiloxane and argon plasmas, followed by oxygen plasma. Disks were analyzed before NTP treatment, immediately after NTP treatment, and after aging for 7, 15, and 30 days. The surface energy of the Y-TZP disks was measured with a goniometer. Quantitative data were submitted to statistical analysis using ANOVA and Tukey’s test (p < 0.05).

Results: Immediately after NTP treatment, the surface energy of the zirconia disks was significantly higher than at any other tested period (p < 0.001), and the water contact angle on the zirconia disks was reduced to 0 degrees. Similar surface energy results were obtained before NTP treatment and after 15 or 30 days of aging (p > 0.05; Tukey’s test). Energy-dispersive spectroscopy results revealed the presence of carbon, oxygen, and silicon on the surface after NTP treatment.

Conclusion: NTP treatment was useful for treating the zirconia surface for cementation procedures, as it produced a high level of hydrophilicity on the zirconia surface. However, this high level of hydrophilicity did not persist after aging.

Full Text PDF File | Order Article

 

 
  © 2022 Quintessence Publishing Co Inc
 

Home | Subscription Services | Books | Journals | Multimedia | Events | Blog
Terms of Use | Privacy Policy | About Us | Contact Us | Advertising | Help | Sitemap | Catalog